Superhydrophobic silica aerogels based on methyltrimethoxysilane precursor
Abstract
The experimental results on the synthesis and physicochemical properties of superhydrophobic silica aerogels, with the highest ever obtained contact angle (~173°), using methyltrimethoxysilane (MTMS) precursor, methanol (MeOH) solvent and ammonium hydroxide (NH4OH) catalyst, are reported. The molar ratios of NH4OH/MTMS (N), H2O/MTMS (H) and MeOH/MTMS (M) were varied from 4.25?×?10?2 to 3.5?×?10?1, 2 to 10 and 1.75 to 17, respectively. It has been found that the gelation time decreases with increase in N and H values and it increases with increase in M values. The bulk density of the aerogels was found to decrease with increase in N, H and M values. It has been observed that the volume shrinkage increases with decrease in N and H values and increases with M values. In the case of catalyst concentration variation, the contact angle (θ) increases slightly from 159° to 167° with increase in N values. On the other hand, in the case of H2O and MeOH variations, the θ first increases from 162° and 160° up to the values of 173° and 167° and then decreases to 160° and 159° with increase in H and M values, respectively. All the MTMS aerogels are opaque to the visible light. The aerogels retain their hydrophobicity up to a temperature of ~480 ° C. The thermal conductivity of the aerogels was found to be around 0.095 W/m?K except for the aerogels with higher bulk density (>0.3 g/cm3, at a lower H value of 2) whose thermal conductivity was around 0.109 W/m?K. The aerogels have been characterized by Fourier transform infrared spectra (FTIR), thermogravimetric and differential thermal analyses (TGA-DTA) and scanning electron microscopy (SEM) techniques. The results have been discussed by taking into account the hydrolysis and condensation reactions and SEM observations.