| Identification | More | [Name]
Lead monoxide | [CAS]
1317-36-8 | [Synonyms]
c.i. 77577
LEAD(+2)OXIDE
LEAD(II) OXIDE
LEAD(II) OXIDE YELLOW
LEAD MONOXIDE
LEAD MONOXIDE, YELLOW
LEAD OXIDE
LEAD OXIDE YELLOW
LITHARGE
RED LEAD
c.i.pigmentyellow46
cipigmentyellow46
leadmonooxide
leadoxide(pbo)
leadprotoxide
Litharge(PbO)
litharge(SnO)
lithargepure
lithargeyellowl-28
massicot | [EINECS(EC#)]
215-267-0 | [Molecular Formula]
OPb | [MDL Number]
MFCD00011164 | [Molecular Weight]
223.2 | [MOL File]
1317-36-8.mol |
| Chemical Properties | Back Directory | [Appearance]
light yellow-orange powder | [Melting point ]
886 °C(lit.)
| [Boiling point ]
1470 °C
| [density ]
9.53 | [vapor pressure ]
10 mm Hg ( 0 °C)
| [refractive index ]
2.67 | [storage temp. ]
Store below +30°C. | [solubility ]
Soluble in concentrated alkali, HCl and ammonium chloride. Insoluble in dilute alkali and alcohol. | [form ]
powder
| [color ]
yellow
| [Specific Gravity]
9.53 | [PH]
8-9 (100g/l, H2O, 20℃)(slurry) | [Stability:]
Stable. Reacts violently with hydrogen peroxide, strong oxidizing agents, aluminium, zirconium, halogens, sulphur trioxide, boron, silicon, sodium, zinc. | [Water Solubility ]
Soluble in concentrated alkali, hydrochloric acid, and ammonium chloride. Insoluble in water, dilute alkali and alcohol. | [Hydrolytic Sensitivity]
4: no reaction with water under neutral conditions | [Merck ]
14,5413 | [Exposure limits]
ACGIH: TWA 0.05 mg/m3
NIOSH: IDLH 100 mg/m3; TWA 0.050 mg/m3 | [CAS DataBase Reference]
1317-36-8(CAS DataBase Reference) | [NIST Chemistry Reference]
Lead monoxide(1317-36-8) | [EPA Substance Registry System]
1317-36-8(EPA Substance) |
| Safety Data | Back Directory | [Hazard Codes ]
T,N | [Risk Statements ]
R61:May cause harm to the unborn child.
R20/22:Harmful by inhalation and if swallowed .
R33:Danger of cumulative effects.
R50/53:Very Toxic to aquatic organisms, may cause long-term adverse effects in the aquatic environment .
R62:Possible risk of impaired fertility. | [Safety Statements ]
S53:Avoid exposure-obtain special instruction before use .
S45:In case of accident or if you feel unwell, seek medical advice immediately (show label where possible) .
S60:This material and/or its container must be disposed of as hazardous waste .
S61:Avoid release to the environment. Refer to special instructions safety data sheet . | [RIDADR ]
UN 2291 6.1/PG 3
| [WGK Germany ]
3
| [RTECS ]
OG1750000
| [TSCA ]
Yes | [HazardClass ]
6.1(b) | [PackingGroup ]
III | [HS Code ]
28241000 | [Hazardous Substances Data]
1317-36-8(Hazardous Substances Data) |
| Hazard Information | Back Directory | [General Description]
Odorless gray or yellow green or red-brown solid. Sinks in water. | [Reactivity Profile]
LITHARGE has weak oxidizing or reducing powers. Redox reactions can however still occur. The majority of compounds in this class are slightly soluble or insoluble in water. If soluble in water, then the solutions are usually neither strongly acidic nor strongly basic. These compounds are not water-reactive. Aluminum carbide is oxidized with incandescence on warming with lead oxide, [Mellor, 1946, Vol. 5, 872]. Mixtures of lead oxide with aluminum powder(as with other metals: sodium, zirconium) give a violent explosions, [Mellor, 1946, Vol. 5, 217, 1941]. | [Health Hazard]
General symptoms of lead poisoning (delayed). Inhalation or ingestion causes abdominal pain (lead colic), metallic taste in mouth, loss of weight, pain in muscles, and muscular weakness. Dust may irritate eyes. | [Description]
Lead(II) oxide occurs in two polymorphs, red, having a tetragonal crystal structure and yellow, having an orthorhombic crystal structure. Both forms occur naturally as rare minerals. The red form is known as “Litharge” and the yellow form is known as “Massico”. | [Physical properties]
The oxide exhibits two crystalline modifications, the reddish or orange-red alpha form, known as litharge, and the yellow beta form, massicot. The alpha form constitutes tetragonal crystals while the beta modification is a yellow amorphous powder of orthorhombic crystal structure. The alpha form is stable at ordinary temperatures, converting to the beta form when heated at 489°C; density 9.35 g/cm3 (beta form); Moh’s hardness 2 (alpha form); the oxide melts at 888°C; vaporizes at 1,472°C with decomposition; vapor pressure 1 torr at 943°C and 5 torr at 1,039°C; practically insoluble in water (the solubility of alpha form is 17 mg/L at 20°C and that of beta form 23 mg/L at 22°C); insoluble in ethanol; soluble in dilute nitric acid and alkalies. | [Production Methods]
Lead monoxide is obtained commercially by two processes, Barton process and the Ball Mill process. The Ball-Mill process involves reaction of molten lead with oxygen or air, and in the Barton process atomized molten lead is stirred in a mechanical furnace above 550°C. The molten metal splashed by the stirring paddle comes in contact with air fed into the cover of the furnace through a pipe, thus forming a mist of finely divided lead monoxide. The mist also contains a small amount of unreacted lead. The mist is passed through an upright shaft where a major portion of unreacted lead falls back into the furnace. It is then rapidly cooled and collected in condensing chambers. The crude product may contain 1 to 3% lead. It is finely ground and sold. The remaining lead in the crude product may be converted into the lead monoxide by stirring the molten mass in presence of air for several hours. The hot product is then cooled rapidly to a temperature below 300°C to prevent any formation of lead tetroxide, Pb3O4.
In an alternate process, a variation of the above method, molten lead is atomized in a shaft furnace. An air stream carries the very finely divided metal into the hot zone of the shaft furnace where the metal evaporates and oxidizes producing very finely divided lead monoxide. The product is passed through the cold zone of the furnace and cooled rapidly. The product obtained is a yellow powdery material, the beta form of lead oxide, massicot, consisting of orthorhombic crystals.
The red lead oxide (the tetragonal alpha modification) is obtained by slow cooling of the lead monoxide melt. The solidified mass may contain the red alpha form of the oxide resulting from slow cooling of the melt, under an outer layer of yellow beta form that may result from the rapid cooling of the outer portion.
Lead monoxide also is produced by a modified Ball Mill process in which high purity lead balls placed in the mill are partially oxidized to produce black or grey oxide. Both the red and yellow form of the oxide may be prepared by alkaline dehydration of lead hydroxide, Pb(OH)2. | [Flammability and Explosibility]
Notclassified | [Purification Methods]
Higher oxides are removed by heating under vacuum at 550o with subsequent cooling under vacuum. It is red at room temperature but becomes yellow at high temperatures (~480o) reversibly. [Ray & Ogg J Am Chem Soc 78 5994 1956, Kwestroo et al. J Inorg Nucl Chem 29 39 1967.] |
| Questions And Answer | Back Directory | [Chemical properties]
Lead monoxide is a yellow tetragonal powder; insoluble in water and ethanol; soluble in acetone, nitric acid, caustic soda and ammonium chloride.
It is amphoteric oxide and thus dissolves both in acids and in alkalies.
PbO + 2HNO3-->Pb(NO3)2+ H2O
PbO+ 2NaOH -->Na2PbO2(Sod. plumbite)+ H2O
On heating in air at 470°C it changes into red lead.
6PbO +O2-->2Pb3O4(red lead) | [Uses]
1. Lead oxide is Mainly used in electron tubes, picture tubes, optical glass, anti-X-ray lead glass and radiation-resistant rubber products.
2. Used in smelting metal lead and preparing lead glass, lead compound, catalyst and paint drier.
3. Used as analytical reagents, silicate flux, but also for the precipitation of amino acids
4. Lead oxide is used in the manufacture of PVC plastic stabilizer and also is the raw materials of other lead salts. In the paint industry, it can be used with oil to make lead soap for paint driers. It can also be used in the manufacture of high refractive index optical glass, ceramic enamel, plane grinding agent of precision machine tool, medical raw materials and rubber coloring agent. It is also used for battery plate manufacturing, oil refining and so on.
5. Used as pigments, metallurgical fluxes and paint driers, and also used in petroleum, rubber, glass, enamel and other industries
6. Used as fluxing agents of decomposing silicate and metallurgy and paint driers, and also used for determination of gold and silver and precipitation of amino acids. It can be blended with glycerol to produce hard materials as adhesives in glass and rubber industry. | [applications]
Lead(II) Oxide is used as the starting material in the synthesis of Dibasic Lead Phthalate Hydrate (D417070); a compound that is used in vinyl wire insulation as a flame retardant.
The principal use of lead monoxide is in the manufacture of pastes for the grids used in lead-acid batteries. It is also widely used in optical, electrical, and electronic glasses, as well as in glazes for fine tableware.To render the lead compounds insoluble in foods, the glazes and vitreous enamels are prepared from frits, in which the lead monoxide is converted to lead bisilicate, for example.
Litharge is also used in rubber as a vulcanizing agent, in lead soaps employed as driers in varnishes, in high-temperature lubricants, as a neutralizing agent in organic syntheses, as a heat stabilizer in plastics, and as a starting material in the production of pigments. The preparation, properties, and other uses of lead oxide are described in. | [Toxicity]
(1) see lead monoxide
(2) The early poisoning symptom is that lead lines appear on the edge of the gums, which may not appear when obviously poisoning, and the skin is soil gray. Neurasthenic syndrome will also emerge in the early period of poisoning. The cerebellar poisoning can result in lead poisoning depression, lead poisoning mania, as well as lead toxicity and paralysis sensitivity multiple neuritis. The lead poisoning can also cause hypochromic anemia and metabolic and endocrine disorders. Moreover, the lead poisoning can inhibit the activity of certain enzymes in digestive system and cause indigestion, abdominal severe pain and liver damage. And it can also cause high blood pressure and cholesterol increasing.
If there is severe abdominal pain, some measures can be taken, such as subcutaneous injection of atropine and other drugs, abdominal warm, enema, hot water bath and so on.
The maximum allowable concentration in air is 0.01 mg/m3.
Wearing mask in operation can block 95% to 97% of lead dust. When steam concentration is high, the filter-type gas mask or hose-type gas masks can be used to mandatorily supply fresh air. In the workplace, eating and smoking are prohibited during working hours. It is essential to take a shower after work and gargle and brush your teeth before meals and after work. After bathing, the lead on the hands or other contaminated parts should also be washed with 1% acetic acid solution. People who have symptoms of lead poisoning should be temporarily out of work, and serious people should be exchanged to the operating post long-termly exposed to lead. | [production]
(1) Lead oxidation method: heat lead for melting to make lead tablets, and then grind at 170~210℃ and roast for oxidation at high temperature above 600℃. The oxide products are grind to obtain the finished lead oxide.
2Pb + O2-->2PbO
(2) The lead oxidation method sees "lead monoxide".Lead monoxide can also be prepared by heating lead nitrate or lead carbonate as:
2Pb(NO3)2-->2PbO+ 4NO2+O2
PbCO3-->PbO +CO2 |
|
|