POLY(ETHYL ACRYLATE)
|
|
POLY(ETHYL ACRYLATE) Eigenschaften
- Dichte
- 1.21 g/mL at 25 °C
- Tg
- -24
- Dampfdichte
- 1.2 (vs air)
- Brechungsindex
- n
20/D 1.469
- Flammpunkt:
- 75 °F
- storage temp.
- Flammables area
- Aggregatzustand
- Solution in toluene (Unit weight does not include weight of solvent.)
- EPA chemische Informationen
- Ethyl acrylate homopolymer (9003-32-1)
Sicherheit
- Risiko- und Sicherheitserkl?rung
- Gefahreninformationscode (GHS)
Kennzeichnung gef?hrlicher | T,F,Xn | ||
---|---|---|---|
R-S?tze: | 11-23/24/25-36/37/38-10-67-65-48/20-38-63 | ||
S-S?tze: | 16-26-28-36/37/39-45-62-36/37 | ||
RIDADR | UN 1993 3/PG 2 | ||
WGK Germany | 3 | ||
Selbstentzündungstemperatur | 997 °F |
Bildanzeige (GHS) | |||||||||||||||||||||||||||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Alarmwort | Achtung | ||||||||||||||||||||||||||||||||||||||||||
Gefahrenhinweise |
|
||||||||||||||||||||||||||||||||||||||||||
Sicherheit |
|
POLY(ETHYL ACRYLATE) Chemische Eigenschaften,Einsatz,Produktion Methoden
R-S?tze Betriebsanweisung:
R11:Leichtentzündlich.R23/24/25:Giftig beim Einatmen, Verschlucken und Berührung mit der Haut.
R36/37/38:Reizt die Augen, die Atmungsorgane und die Haut.
R10:Entzündlich.
S-S?tze Betriebsanweisung:
S16:Von Zündquellen fernhalten - Nicht rauchen.S26:Bei Berührung mit den Augen sofort gründlich mit Wasser abspülen und Arzt konsultieren.
S28:Bei Berührung mit der Haut sofort abwaschen mit viel . . . (vom Hersteller anzugeben).
S36/37/39:Bei der Arbeit geeignete Schutzkleidung,Schutzhandschuhe und Schutzbrille/Gesichtsschutz tragen.
S45:Bei Unfall oder Unwohlsein sofort Arzt zuziehen (wenn m?glich, dieses Etikett vorzeigen).
Chemische Eigenschaften
clear solutionVerwenden
Acrylate elastomers are widely used in the automotive industry for seals in automatic transmissions, valve stems, crankshafts, oil pans, and packings. Other uses include hose, tubes, boots, spark plugs, and fabric coatings.Vorbereitung Methode
Acrylates can be polymerized in a variety of ways including bulk, solution, suspension, and emulsion polymerization. The most common industrial methods are suspension and emulsion polymerization. The three major backbone monomers used in acrylate elastomers are ethyl acrylate, butyl acrylate, and methoxyethyl acrylate.POLY(ETHYL ACRYLATE) Upstream-Materialien And Downstream Produkte
Upstream-Materialien
Downstream Produkte
POLY(ETHYL ACRYLATE) Anbieter Lieferant Produzent Hersteller Vertrieb H?ndler.
Global( 46)Lieferanten
Firmenname | Telefon | Land | Produktkatalog | Edge Rate | |
---|---|---|---|---|---|
Hubei Jusheng Technology Co.,Ltd. | 18871490254 |
linda@hubeijusheng.com | CHINA | 28172 | 58 |
Hubei xin bonus chemical co. LTD | 86-13657291602 |
linda@hubeijusheng.com | CHINA | 22963 | 58 |
Chongqing Chemdad Co., Ltd | +86-023-6139-8061 +86-86-13650506873 |
sales@chemdad.com | China | 39894 | 58 |
Shaanxi Dideu Medichem Co. Ltd | +86-029-81138252 +86-18789408387 |
1057@dideu.com | China | 3886 | 58 |
Zhengzhou Alfa Chemical Co.,Ltd | +8618530059196 |
sale04@alfachem.cn | China | 11839 | 58 |
Dideu Industries Group Limited | +86-29-89586680 +86-15129568250 |
1026@dideu.com | China | 22787 | 58 |
Alfa Chemistry | |
Info@alfa-chemistry.com | United States | 24072 | 58 |
Hebei Fengjia New Material Co., Ltd | +86-0311-87836622 +86-17333973358 |
sales06@hbduling.cn | China | 8051 | 58 |
Shanghai Acmec Biochemical Technology Co., Ltd. | +undefined18621343501 |
product@acmec-e.com | China | 33338 | 58 |
SHANGHAI KEAN TECHNOLOGY CO., LTD. | +8613817748580 |
cooperation@kean-chem.com | China | 40066 | 58 |
9003-32-1()Verwandte Suche:
Phenylselenol
Tris(pentan-2,4-dionato)eisen(II)
Kupfer(II)-4-oxopent-2-en-2-olat
Benzylisocyanid
(Pentan-2,4-dionato-O,O')silber
Ethylisocyanacetat
N-Butylisocyanid
Aluminiumtris(2,4-pentandionato-O,O')
Tris(2,2,6,6-tetramethylheptan-3,5-dionato-O,O')dysprosium
Methylisocyanacetat
(p-Toluolsulfonyl)methylisocyanid
1,1,3,3-Tetramethylbutylisocyanat
Dichloro(ethylendiamin)platin
Tris(2,2,6,6-tetramethylheptan-3,5-dionato-O,O')europium
(Ethylenbis(nitrilomethylidyn)-2,2'-diphenolato)cobalt(II)
2-Methylpropylisocyanid
Ethylacrylat
- 2-Propenoicacid,ethylester,homopolymer
- Ethyl2-propenoate,homopolymer
- Ethylacrylate,homopolymer
- Poly(acrylicacid,ethylester)
- POLY(ETHYL ACRYLATE)
- ETHYL ACRYLATE LATEX
- ETHYL ACRYLATE RESIN
- POLY(ETHYL ACRYLATE), SOLUTION IN TOLUEN E, AVERAGE MW CA. 95,000 (GPC)
- POLY(ETHYL ACRYLATE), SECONDARY STANDARD (TOLUENE)
- solutionintolueneaveragemwca.95,000(gpc)
- poly(ethyl acrylate) solution
- POLY(ETHYL ACRYLATE), APPROX. 20% SOLUTION IN TOLUENE
- Poly(ethyl acrylate)approx. 20% solution in toluene (M.W. ca. 100,000)
- Poly(ethyl acrylate) solution average Mw ~95,000 by GPC, in toluene
- POLY(ETHYL ACRYLATE) ISO 9001:2015 REACH
- Poly(ethyl 2-propenoate)
- 9003-32-1
- Polymers
- Acrylate Polymers
- Acrylics
- Hydrophobic Polymers
- Acrylate Polymers
- Hydrophobic Polymers
- Materials Science
- Polymer Science