| Identification | Back Directory | [Name]
POLY(VINYLIDENE FLUORIDE-CO-HEXAFLUOROPROPYLENE) | [CAS]
9011-17-0 | [Synonyms]
PVDF-HFP
HEXAFLUOROPROPENE POLYMER
Vinylidene Fluoride-hexafluoropropylene
1,1-Difluoroethylene-perfluoropropene copolymer
Hexafluoropropylene-vinylidene fluoride: (Viton)
vinylidene fluoride/ hexafluoropropene copolymer
POLY(VINYLIDENE FLUORIDE-CO-HEXAFLUOROPROPYLENE)
HEXAFLUOROPROPYLENE-VINYLDENE-FLUORIDE,COPOLYMER
HEXAFLUOROPROPYLENE-VINYLIDENEFLUORIDE,COPOLYMER
Vinylidene fluoride-Hexafluoropropylene copolymer
Hexafluoropropylene-vinylidenefluoridecopolymer2641
Poly(vinylidene fluoride-co-hexafluoropropylene) pellets
1,1-Difluoroethylene-1,1,2,3,3,3-hexafluoropropene copolymer
1-Propene,1,1,2,3,3,3-hexafluoro-,polymerwith1,1-difluoroethene
POLY(VINYLIDENE FLUORIDE-CO-HEXAFLUORO-P ROPYLENE), MELT INDEX 4-10
POLY(VINYLIDENE FLUORIDE-CO-HEXAFLUORO-P ROPYLENE), AVERAGE MN CA. 130,000
POLY(VINYLIDENE FLUORIDE-CO-HEXAFLUORO-P ROPYLENE), AVERAGE MN CA. 110,000
Poly(vinylidene fluoride-co-hexafluoropropylene) average Mw ~400,000, average Mn ~130,000, pellets
Poly(vinylidene fluoride-co-hexafluoropropylene) average Mw ~455,000, average Mn ~110,000, pellets | [Molecular Formula]
(-CH2CF2-)x[-CF2CF(CF3)-]y | [MDL Number]
MFCD00212573 | [MOL File]
9011-17-0.mol | [Molecular Weight]
214.06 |
| Hazard Information | Back Directory | [Uses]
Wire and cable coatings, flexible and corrosion-resistant tubing, and liners for pipes and tanks. | [Chemical Properties]
A primary advantage of fluororubber is its exceptional heat,
chemical, and solvent resistance. The copolymer is biologically
inert. The decomposition products of FPM depend
on the chemical composition of the intact polymer and also
on the conditions under which it is decomposed. The temperature
to which the polymer is subjected, the atmosphere in
which decomposition occurs, and the material of the vessel
used can alter the kinds and quantities of the decomposition
products. When a copolymer of vinylidene fluoride and
hexafluoropropylene decomposed at 550 and 800°C, carbon
monoxide and carbon dioxide were produced. Hydrogen
fluorides and other fluorocarbons have been reported as
decomposition products. | [Preparation]
The usual commercial practice is to mix the rubber on a mill with the
diamine derivative, together with filler (such as carbon black or silica) and a
metal oxide. The compounded stock is then given a short press cure (typically, 0.5 hours at 150??C) and a long oven cure (typically, 24 hours at 200??C).
The reactions which occur in the vulcanization of vinylidene fluoridehexafluoropropylene copolymers have been extensively studied and a
three-stage process is thought to be involved. The first step is postulated as
the elimination of hydrogen fluoride from the polymer upon treatment with a
base. Probably the tertiary fluorine atom of the hexafluoropropylene unit is
the most readily removed. The initially formed double bonds then activate
the elimination of hydrogen fluoride from neighbouring groups to give a
conjugated system:
Elimination is thought to be catalysed by basic materials, such as magnesium oxide, which are commonly included in commercial formulations.
Elimination takes place rapidly and probably occurs during milling when a
diamine curing system is used. Evidence for the presence of unsaturation in
amine-treated vinylidene fluoride-hexafluoropropylene copolymer comes
from the infrared spectrum of the material.
The second step in the vulcanization process is regarded as involving
addition of the curing agent at the sites of unsaturation. With a diamine
This reaction occurs during the press cure operation.
The third step in the vulcanization process is considered to involve the
elimination of hydrogen fluoride to form a diimine:
If this is the case, it would be necessary to remove all the water present in
order to force the equilibrium completely toward diimine formation and the
establishment of permanent cross-links. Experimental evidence for this proposition is that a full state of cure is not attained if the long heating process is
carried out in the mould, i.e. in a virtually closed system. Hydrolysis is also
demonstrated by the fact that much of the diamine present in a vulcanizate
can be extracted by treatment with water. It may be noted here that
vinylidene fluoride-hexafluoropropylene copolymers which are peroxidecurable do not lead to water formation and so give vulcanizates with reduced
porosity.
Vulcanized vinylidene fluoride-hexafluoropropylene copolymers show excellent resistance to oils and fuels, both at room temperature and at elevated
temperature. Vulcanizates also have good resistance to most solvents, although polar solvents such as esters and ketones cause high swelling.
Vinylidene fluoride-hexafluoropropylene copolymer vulcanizates have excellent thermal stability, withstanding long periods at 250??C without serious
deterioration. Low temperature performance is limited and the elastomers
are not generally suitable for sub-zero use. Applications of the elastomers
include seals and hose in contact with fuels and lubricants, pump components
and tank linings.
A terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene is also available and gives vulcanizates with improved resistance to heat ageing. | [Production Methods]
Vinylidene fluoride-based elastomers have generally been
prepared by free-radical emulsion polymerization of the
monomers with organic or inorganic peroxide initiators.
Low-molecular-weight fluid or semifluid polymers have
been made with various chain transfer agents, special initiators,
or dehydrofluorination oxidation methods. |
|
| Company Name: |
Sigma-Aldrich
|
| Tel: |
021-61415566 800-8193336 |
| Website: |
https://www.sigmaaldrich.cn |
| Company Name: |
Rhawn Reagent
|
| Tel: |
400-400-1332688 18019345275 |
| Website: |
http://www.rhawn.cn |
|